Imam Riva'I, Ika Oktavia Wulandari, Hermin Sulistyarti, Akhmad Sabarudin
In this study, the synthesis of Fe3O4 nanoparticles was done with surface modification using PVA with coprecipitation-ultrasonication method. Time variations and PVA concentrations were added to determine the effect on crystallite size and lattice parameters on the synthesis of Fe3O4-PVA nanoparticles. Fe3O4 characterization was done using X-Ray Diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FTIR) instruments. FTIR was employed to determine PVA coating on the surface of Fe3O4 nanoparticles. The crystallite size and lattice parameters were analyzed using XRD. From the FTIR data, it is known that the interaction between PVA and Fe3O4 nanoparticles is characterized by Fe-O-C group at 1100 cm-1 region which is characteristic of Fe3O4-PVA nanoparticles, C-H groups of PVA in the range of 2950 cm-1 wave number, C-C of PVA regions of wave number 1405 cm-1, Fe3O4 and Fe3O4-PVA samples are in the range of 565 cm-1. In addition, the variation of ultrasonication time and the addition of PVA concentration have an effect on the crystallite size change and the lattice parameter observed from the XRD data. The use of ultrasonication time will affect the size of the crystallite become smaller and the grating lattice parameters obtained are wider. The effect of addition of PVA showed that higher concentration of PVA resulted in smaller crystallite size and larger lattice parameters. These results indicated that ultrasonication time and addition of PVA concentration greatly affect the characteristics of nanoparticles. © Published under licence by IOP Publishing Ltd.
Department of Chemistry, Faculty of Science, Brawijaya University, Jl Veteran, Malang, 65145, Indonesia; Research Center for Advanced System and Material Technology (ASMAT), Brawijaya University, Malang, 65145, Indonesia